This study will evaluate and compare the effect of the amount of toothpaste used and brushing time on enamel strengthening (percent of surface microhardness recovery, % SMHR) and enamel fluoride uptake (EFU).
Study Type
INTERVENTIONAL
Allocation
RANDOMIZED
Purpose
TREATMENT
Masking
SINGLE
Enrollment
65
Dentifrice containing 1150 parts per million (ppm) fluoride as sodium fluoride / silica and 0.4% carbopol
Dentifrice containing 1150 ppm fluoride as sodium fluoride / silica and 0.4% carbopol
Dentifrice containing 250 ppm fluoride as sodium fluoride / silica and 0.4% carbopol
Indiana University School of Dentistry
Indianapolis, Indiana, United States
Percentage Surface Micro Hardness Recovery (% SMH), of Brushing for 2 Minutes Versus (vs.) Brushing for 45 Seconds With 1.5g of Experimental Dentifrice.
SMH recovery test was used to assess the changes in mineralization status of enamel specimens using a Wilson 2100 Hardness tester. SMH recovery was performed in-vitro and determined by measuring the length of the indentations of enamel specimens. An increase in the indentation length compared to the baseline indicates softening while decrease in the indentation length represents re-hardening of enamel surface. % SMH recovery was calculated from indentation length (micrometer \[μm\]) of sound enamel specimen at baseline (B), indentation length (μm) after in vitro demineralization (D1), indentation length (μm) after intra-oral exposure (R): \[D1-R/D1-B\] ×100.
Time frame: At Baseline and at Day 14
Percentage Surface Micro Hardness (% SMH) Recovery , of Brushing for 2 Minutes vs. Brushing for 45 Seconds With 0.5g of Experimental Dentifrice.
SMH recovery test was used to assess the changes in mineralization status of enamel specimens using a Wilson 2100 Hardness tester. SMH recovery was performed in-vitro and determined by measuring the length of the indentations of enamel specimens. An increase in the indentation length compared to the baseline indicates softening while decrease in the indentation length represents re-hardening of enamel surface. % SMH recovery was calculated from indentation length (μm) of sound enamel specimen at baseline (B), indentation length (μm) after in vitro demineralization (D1), indentation length (μm) after intra-oral exposure (R): \[D1-R/D1-B\] ×100.
Time frame: At Baseline and at Day 14
Percentage Surface Micro Hardness (% SMH) Recovery, of Brushing for 2 Minutes With 0.5g of Experimental Dentifrice vs. Brushing for 2 Minutes With 1.5g of Experimental Dentifrice.
SMH recovery test was used to assess the changes in mineralization status of enamel specimens using a Wilson 2100 Hardness tester. SMH recovery was performed in-vitro and determined by measuring the length of the indentations of enamel specimens. An increase in the indentation length compared to the baseline indicates softening while decrease in the indentation length represents re-hardening of enamel surface. % SMH recovery was calculated from indentation length (μm) of sound enamel specimen at baseline (B), indentation length (μm) after in vitro demineralization (D1), indentation length (μm) after intra-oral exposure (R): \[D1-R/D1-B\] ×100.
This platform is for informational purposes only and does not constitute medical advice. Always consult a qualified healthcare professional.
A non fluoride dentifrice was given to participants of each arm at washout period
Time frame: At Baseline and at Day 14
Percentage Surface Micro-hardness Recovery (% SMH), of Brushing for 45 Seconds With 0.5g of Experimental Dentifrice vs. Brushing for 45 Seconds With 1.5g of Experimental Dentifrice.
SMH recovery test was used to assess the changes in mineralization status of enamel specimens using a Wilson 2100 Hardness tester. SMH recovery was performed in-vitro and determined by measuring the length of the indentations of enamel specimens. An increase in the indentation length compared to the baseline indicates softening while decrease in the indentation length represents re-hardening of enamel surface. % SMH recovery was calculated from indentation length (μm) of sound enamel specimen at baseline (B), indentation length (μm) after in vitro demineralization (D1), indentation length (μm) after intra-oral exposure (R): \[D1-R/D1-B\] ×100.
Time frame: At Baseline and at Day 14
Percent Surface Micro-hardness (% SMH) Recovery, of Brushing for 2 Minutes With 1.5g of Experimental Dentifrice vs. Brushing for 2 Minutes With 1.5g of an Control Dentifrice.
SMH recovery test was used to assess the changes in mineralization status of enamel specimens using a Wilson 2100 Hardness tester. SMH recovery was performed in-vitro and determined by measuring the length of the indentations of enamel specimens. An increase in the indentation length compared to the baseline indicates softening while decrease in the indentation length represents re-hardening of enamel surface. % SMH recovery was calculated from indentation length (μm) of sound enamel specimen at baseline (B), indentation length (μm) after in vitro demineralization (D1), indentation length (μm) after intra-oral exposure (R): \[D1-R/D1-B\] ×100.
Time frame: At Baseline and at Day 14
Enamel Fluoride Uptake (EFU) After Brushing for 2 Minutes vs. Brushing for 45 Seconds With 1.5g of Experimental Dentifrice.
EFU was measured by using micro-drill analysis of the enamel specimens carried out after 14 days of intra-oral exposure for each of the toothpaste treatments. The amount of fluoride-uptake by enamel was calculated based on the amount of fluoride divided by the area of the enamel cores.
Time frame: At Day 14
Enamel Fluoride Uptake (EFU) After Brushing for 2 Minutes vs. Brushing for 45 Seconds With 0.5g of Experimental Dentifrice.
EFU was measured by using micro-drill analysis of the enamel specimens carried out after 14 days of intra-oral exposure for each of the toothpaste treatments. The amount of fluoride-uptake by enamel was calculated based on the amount of fluoride divided by the area of the enamel cores.
Time frame: At Day 14
Enamel Fluoride Uptake (EFU) After Brushing for 2 Minutes With 0.5g of Experimental Dentifrice vs. Brushing for 2 Minutes With 1.5g of Experimental Dentifrice.
EFU was measured by using micro-drill analysis of the enamel specimens carried out after 14 days of intra-oral exposure for each of the toothpaste treatments. The amount of fluoride-uptake by enamel was calculated based on the amount of fluoride divided by the area of the enamel cores.
Time frame: At Day 14
Enamel Fluoride Uptake (EFU) After Brushing for 45 Seconds With 0.5g of Experimental Dentifrice vs. Brushing for 45 Seconds With 1.5g of Experimental Dentifrice.
EFU was measured by using micro-drill analysis of the enamel specimens carried out after 14 days of intra-oral exposure for each of the toothpaste treatments. The amount of fluoride-uptake by enamel was calculated based on the amount of fluoride divided by the area of the enamel cores.
Time frame: At Day 14
Enamel Fluoride Uptake (EFU) After Brushing for 2 Minutes With 1.5g of Experimental Dentifrice vs. Brushing for 2 Minutes With 1.5g of Control Dentifrice.
EFU was measured by using micro-drill analysis of the enamel specimens carried out after 14 days of intra-oral exposure for each of the toothpaste treatments. The amount of fluoride-uptake by enamel was calculated based on the amount of fluoride divided by the area of the enamel cores.
Time frame: At Day 14